Chemical Composition
The chemical composition of hastelloy (r) G50(r) is outlined in the following table.
Elements | Content (%) |
---|---|
Nickel, Ni | ≥ 50 |
Chromium, Cr | 19-21 |
Iron, Fe | 15-20 |
Molybdenum, Mo | 8-10 |
Cobalt, Co | ≤ 2.50 |
Manganese, Mn | ≤ 1 |
Silicon, Si | ≤ 1 |
Tungsten, W | ≤ 1 |
Niobium, Nb | ≤ 0.50 |
Copper, Cu | ≤ 0.50 |
Aluminum, Al | ≤ 0.40 |
Phosphorous, P | ≤ 0.040 |
Carbon, C | ≤ 0.020 |
Sulfur, S | ≤ 0.015 |
Physical properties
The physical properties of hastelloy(r) G50(r) are given in the following table.
Properties | Metric | Imperial |
---|---|---|
Density | 8.33 g/cm³ | 0.301 lb/in³ |
Melting point | 1399°C | 2550°F |
Mechanical Properties
The following table shows the mechanical properties of Hastelloy(r) G50(r).
Properties | Metric | Imperial |
---|---|---|
Tensile strength | ≥ 760 MPa | ≥ 110000 psi |
Yield strength (@ strain 0.200%) | 700-860 MPa | 102000-125000 psi |
Elastic modulus (room temp.) | 192 GPa | 27800 ksi |
Elongation at break (in 50 mm) | ≥ 20% | ≥ 20% |
Hardness, Brinell (estimated from Rockwell C for Brinell 10 mm ball/3000 kg load) | 290 | 290 |
Hardness, Knoop (estimated from Rockwell C) | 345 | 345 |
Hardness, Rockwell A (estimated from Rockwell C) | 66 | 66 |
Hardness, Rockwell C | ≤ 31 | ≤ 31 |
Hardness, Vickers (estimated from Rockwell C) | 300 | 300 |